PdFe/Ir(111) has attracted tremendous attention for next-generation spintronics devices due to existence of magnetic skyrmions with the external magnetic field. Our density functional theoretical calculations in combination with spin dynamics simulation suggest that the spin spiral phase in fcc stacked PdFe/Ir(111) flips into the skyrmion lattice phase around Bext∼ 6 T. This leads to the microscopic understanding of the thermodynamic and kinetic behaviours affected by the intrinsic spin-lattice couplings (SLCs) in this skyrmion material for magneto-mechanical properties. Here we calculate fully relativistic SLC parameters from first principle computations and investigate the effect of SLC on dynamical magnetic interactions in skyrmion multilayers PdFe/Ir(111). The exchange interactions arising from next nearest-neighbors (NN) in this material are highly frustrated and responsible for enhancing skyrmion stability. We report the larger spin-lattice effect on both dynamical Heisenberg exchanges and Dzyaloshinskii-Moriya interactions for next NN compared to NN which is in contrast with recently observed spin-lattice effect in bulk bcc Fe and CrI3 monolayer. Based on our analysis, we find that the effective measures of SLCs in fcc (hcp) stacking of PdFe/Ir(111) are ∼2.71(∼2.36) and ∼14.71(∼21.89) times stronger for NN and next NN respectively, compared to bcc Fe. The linear regime of displacement for SLC parameters is ≤ 0.02 Å which is 0.72\% of the lattice constant for PdFe/Ir(111). The microscopic understanding of SLCs provided by our current study could help in designing spintronic devices based on thermodynamic properties of skyrmion multilayers.
Author indications on fulfilling journal expectations
Provide a novel and synergetic link between different research areas.
Open a new pathway in an existing or a new research direction, with clear potential for multi-pronged follow-up work
Detail a groundbreaking theoretical/experimental/computational discovery
Present a breakthrough on a previously-identified and long-standing research stumbling block